دانشگاه صنعتی شریف مجله ی مهندسی عمران شریف 2676-4768 38.2 1.1 2022 05 22 Investigating the influence of parent concrete on mechanical properties of recycled concrete مطالعه ی اثر خواص بتن مادر بر پارامترهای مکانیکی بتن بازیافتی 47 57 22598 10.24200/j30.2021.57419.2909 FA حسن صالحی دانشکده ی مهندسی مکانیک، دانشگاه پدافند هوایی خاتم‌الانبیاء(ص) نادر بیگلری جو دانشکده ی مهندسی عمران، دانشگاه عمران توسعه همدان هوشنگ برخورداری دانشکده ی مهندسی مکانیک، دانشگاه پدافند هوایی خاتم الانبیاء (ص) Journal Article 2021 04 03 One of the most significant concerns of recent years among scientists has been related to waste management actions and policies. Unfortunately, landfills are filled with various debris and demolition from old building including waste concrete, glass, brick, ceramic, and plastic. Waste concrete seems to occupy a large volume of these landfills; thus, they are potentially among the most appropriate choices for recycling process. However, different papers have focused on the impact of recycled concrete aggregates in concrete and in recent years, no specific model has been recommended to predict the behavior of parent concrete in recycled concrete. In this study, a central composite design along with response surface methodology was employed to prepare experimental designs and model the properties of concrete made of recycled aggregates. Effective factors included compressive strength of parent concrete, substitution rate of parent concrete, and value of cement, while the compressive strength, tensile strength, and water absorption of recycled concrete were introduced as goal responses. Based on the statistical analysis, all recommended models were adequate with acceptable coefficient of determination ( ). Response surface and perturbation plots revealed that compressive strength, tensile strength, and water absorption of recycled concretes depended heavily on the compressive strength of parent concrete. Moreover, in order to generate concretes with higher compressive strength than the compressive strength of parent concrete, the value of compressive strength for parent concrete should be above MPa. However, for low-strength parent concretes, substitution rate should be limited in order to reduce undesirable performance. As the compressive strength of recycled concrete aggregates increased from to MPa, the compressive strength of recycled concrete was enhanced by over percent. In this substitution, water absorption reduced over percent. Additionally, when the compressive strength of recycled aggregates was fixed at MPa, by changing substitution rate from % to %, the compressive strength of recycled concrete increased from to MPa. The tensile strength of recycled concrete also was enhanced from to MPa. با وجود انجام مطالعات فراوان در زمینه‌ی بتن‌های بازیافتی، تاکنون درخصوص تأثیر مقاومت بتن مادر در بتن‌های بازیافتی مدلی ارائه نشده است. ارائه‌ی مدل در طرح‌های بتنی می‌تواند از صرف هزینه و زمان مازاد برای ساخت آن‌ها جلوگیری کند. هدف از مطالعه‌ی حاضر، ارائه‌ی یک مدل ریاضی برای پیش‌بینی رفتار مکانیکی بتن بازیافتی با استفاده از روش طراحی آزمایش مرکب مرکزی و تحلیل آماری سطح پاسخ است. پارامترهای مؤثر ورودی، شامل: مقاومت فشاری بتن مادر، درصد جایگزینی و عیار سیمان بوده است. نتایج نشان می‌دهند که مقاومت فشاری، مقاومت کششی و جذب آب بتن‌های بازیافتی به شدت وابسته به مقاومت فشاری بتن مادر هستند. با افزایش مقاومت فشاری شن بازیافتی از ۱۹ به ۳۶ مگاپاسکال، مقاومت فشاری بتن بازیافتی حدود ۴۰\٪ افزایش و جذب آب آن حدود ۳۰\٪ کاهش یافته است. زمانی که مقاومت فشاری بتن مادر بیش از ۲۸ مگاپاسکال است، می‌توان درصد جایگزینی سنگ‌دانه‌ی بازیافتی را افزایش داد و بتن‌هایی با مقاومت بالاتر از بتن مادر تولید کرد. https://sjce.journals.sharif.edu/article_22598_d79bc606792288b59c64959c6bcbf5d5.pdf